You are here: Home » Product Center » Unsaturated polyester resin » Artificial stone resin » WL-8101

WL-8101

Product Properties: WL-8101 is a universal o-benzene resin. Applicable to non-enhanced classes, artificial agate and artificial marble, have excellent coloring performance.

Main Application: WL-8101 Resin is used in artificial agate and artificial marble, with higher breaking elongation and better process, suitable for rapid demolding, and the articles are not easy to crack.


Product Specifications

performance

Scope

unit

standard test

Exterior

Light and transparent

-

GB / T8237-2005

Viscosity 25 ° C

350-500

MPA.s

GB / T7193-2008

Acid value

18-24

Mgkoh / g

GB / T2895-2008

Solid content

66-72

GB / T7193-2008

Gel time 25 ° C

4-6

minutes

GB / T7193-2008

Note: 25 ° C gel time: 100 g of a 0.7 Gwen forest promoter and 1.3G Wenlin curing agent.


Liquid resin performance (typical)

performance

Numerical value

unit

standard test

Storage period (not triggered, dark), 20 ° C

3

-


Resin casting body (typ)

performance

Numerical value

unit

standard test

Tensile Strength

50

MPA

GB / T2567-2008

Tension elastic modulus

2900

MPA

GB / T2567-2008

Fracture elongation

5.0

%

GB / T2567-2008

Bending strength

80

MPA

GB / T2567-2008

Bending elastic modulus

3200

MPA

GB / T2567-2008

Impact strength

12

KJ / M2

GB / T2567-2008

Heat distortion temperature

50

GB / T1634-2004

Curing conditions: 24 hours, 40 ° C, 60 ° C, 80 ° C, respective

2 hours

Test conditions: temperature 23 ± 2 ° C, relative humidity 50 ± 6%


Use instructions and precautions

1. WL-8101 Resin does not include accelerator, and the appropriate amount of accelerator and curing agent must be added according to the operating environment and operational demand.

2. In order to obtain a paraffin-styrene solution to obtain a natural molded surface that the article is in contact with the air.

3. In order to make the product performance, it can be cured after 80 ° C for a few hours.


Storage conditions

1. The resin should be stored in a dry chamber below 25 ° C before use before the original packaging (avoiding the damage to the bucket and bucket).

2. Elevation of temperature and light irradiation will significantly reduce storage, and should avoid direct sunlight and away from heat.

3. Unsaturated polyester resin liquid containing styrene is flammable, and it is far from the fire. Note See Secure Data Sheet.


Storage conditions

1. The resin should be stored in a dry chamber below 25 ° C before use.

2. The increase in temperature and the light irradiation will significantly reduce the storage period, and the direct sunlight and away from the heat source should be avoided.

3. The unsaturated polyester resin liquid containing styrene is flammable, and it is far from the fire. Note See Secure Data Sheet.

All various data are derived from our in-depth research and extensive practice, and thus is completely credible. However, since the production of products is affected by multiple factors, the actual performance, effects and effects of the above data and product specific application and processing, and the direct and indirect losses produced, we are not responsible. Before selecting the above products, please check the quality, performance indicators, security, and other data of the product, and confirm it. At the same time, users should also pay attention to avoid violations of various relevant bills, registered trademarks and patent rights. We are not responsible for this.

 
Hubei Wanglin New Material Technology Co., Ltd. is a new company specializing in the production of unsaturated polyester resins in Hongwanglin New Material Technology Co., Ltd., the company's registered capital of one hundred million yuan, main technological relying on Shandong Wanglin New Material Technology Technology Ltd. and its subordinate production bases.

Quick Navigation

Product Category

Product Inquiry
All rights reserved2022 Hubei Wanglin New Material Technology Co., Ltd. 鲁ICP2020038246号-1