WL-8801

Product Properties: WL-8801 is a universal phenyl-type quartz stone resin. The resin has the advantages of medium viscosity and medium reaction activity, with good toughness, good weather resistance, and wide applicability.

 Main Application: The WL-8801 resin is mainly suitable for normal temperature and medium-temperature-consolidated pyrone products.


Product specifications

performance

Scope

unit

standard test

Exterior

Light and transparent

-

GB / T8237-2005

Viscosity 25 ° C

700-1000

MPA.s

GB / T7193-2008

Acid value

20-27

Mgkoh / g

GB / T2895-2008

Solid content

67-73

GB / T7193-2008

Gel time 25 ° C

6-9

minutes

GB / T7193-2008

Note: 25 ° C gel time: 100 g of a 0.7 Gwen forest promoter and 1.3G Wenlin curing agent.

Liquid resin performance (typical)

performance

Numerical value

unit

standard test

Storage period (not triggered, dark), 20 ° C

3

-


Resin casting body (typ)

performance

Numerical value

unit

standard test

Tensile Strength

50

MPA

GB / T2567-2008

Tension elastic modulus

2600

MPA

GB / T2567-2008

Fracture elongation

9.0

%

GB / T2567-2008

Bending strength

60

MPA

GB / T2567-2008

Bending elastic modulus

2600

MPA

GB / T2567-2008

Impact strength

15

KJ / M2

GB / T2567-2008

Heat distortion temperature

45

GB / T1634-2004

Curing conditions: 24 hours, 40 ° C, 60 ° C, 80 ° C, respective 2 hours

Test conditions: temperature 23 ± 2 ° C, relative humidity 50 ± 6%


Instructions and precautions

1. WL-8810 resin does not contain accelerator, and the appropriate amount of accelerator and curing agent must be added according to the operating environment and operational demand.

2. In order to cure the article from the natural molded surface of the article to air, it is not viscous, and the paraffin-styrene solution is added properly.

3. In order to make the product performance, it can be cured after 80 ° C for a few hours.


Storage conditions

1. The resin should be stored in a dry chamber below 25 ° C before use.

2. The increase in temperature and the light irradiation will significantly reduce the storage period, and the direct sunlight and away from the heat source should be avoided.

3. The unsaturated polyester resin liquid containing styrene is flammable, and it is far from the fire. Note See Secure Data Sheet.


All various data are derived from our in-depth research and extensive practice, and thus is completely credible. However, since the production of products is affected by multiple factors, the actual performance, effects and effects of the above data and product specific application and processing, and the direct and indirect losses produced, we are not responsible. Before selecting the above products, please check the quality, performance indicators, security, and other data of the product, and confirm it. At the same time, users should also pay attention to avoid violations of various relevant bills, registered trademarks and patent rights. We are not responsible for this.


 
Hubei Wanglin New Material Technology Co., Ltd. is a new company specializing in the production of unsaturated polyester resins in Hongwanglin New Material Technology Co., Ltd., the company's registered capital of one hundred million yuan, main technological relying on Shandong Wanglin New Material Technology Technology Ltd. and its subordinate production bases.

Quick Navigation

Product Category

Product Inquiry
All rights reserved2022 Hubei Wanglin New Material Technology Co., Ltd. 鲁ICP2020038246号-1