WL-1930

Product properties

The WL-1930 is a pre-promoting pre-touches the unsaturated polyester resin. The resin has the advantages of good water resistance, high strength, and infiltration with glass fiber.

Main application

The WL-1930 resin is suitable for production processes such as hand paste, jet, etc., and is mainly used to make glass reinforced reinforced reinforcement ships and sinks.

Product specification

performance

scope

unit

standard test

Exterior

Light -colored transparency

-

GB/T8237-2005

Viscosity 25 ℃

260-400

mpa.s

GB/T7193-2008

Acid value

18-26

mgkoh/g

GB/T2895-2008

Solid content

54-60

GB/T7193-2008

Gel time 25 ℃

22-38

minutes

GB/T7193-2008

Note: 25 ° C Gel Time: 100g resin plus 0.7g Wanglin promoter and 1.3g Wanglin curing agent.

Liquid resin performance (typical value)

performance

Value

unit

standard test

Storage period (not caused, dark parts), 20 ℃

3

-

Resin pouring performance (typical value)

performance

Value

unit

standard test

Tensile Strength

62

MPA

GB/T2567-2008

Stretching elastic modulus

3500

MPA

GB/T2567-2008

Fracture extension

2

%

GB/T2567-2008

Bending strength

100

MPA

GB/T2567-2008

Bending elastic modulus

3600

MPA

GB/T2567-2008

Impact strength

12

Kj/m2

GB/T2567-2008

Heat distortion temperature

65

GB/T1634-2004

CIThization conditions: room temperature to curing 24 hours, 40 ° C, 60 ° C, 80 ° C for 2 hours each

Test conditions: temperature 23 ± 2 ℃, relative humidity 50 ± 6 %

Instructions and precautions

1.    The WL-1930 resin contains promoters. When used, it is necessary to add an appropriate amount of promoter and curing agent according to the operating environment and operating needs.

2.    When using, you must pay attention to controlling the water content of glass fiber, filler, pigment paste and other materials, and pay attention to the compatibility of pigment paste and unsaturated polyester resin.

Storage conditions

1.  The resin should be stored in a dry room below 25 ° C before using the resin before using the original packaging (avoid damage to the barrel and barrel).

2.  The increase in temperature and light irradiation will significantly reduce the storage period. Direct sunlight and stay away from the thermal source should be avoided during storage.

3..  The unsaturated polyester resin liquid containing the styrene is flammable, and it should be far away from the bright fire when storing. Pay attention to the security data table.

All kinds of data are derived from our in -depth research and extensive practice, so it is completely credible. However, due to the multiple factors of product production, we are not responsible for the actual performance, effects and impacts caused by the above data and the specific application and processing of the products and the processing of the product, and the direct and indirect losses caused by it. Before selecting the above products, please check the product quality, performance indicators, security and other data and confirm it by themselves. At the same time, users should also pay attention to avoid violations of various relevant bills, registered trademarks and patent rights. We are not responsible for this.



 
Hubei Wanglin New Material Technology Co., Ltd. is a new company specializing in the production of unsaturated polyester resins in Hongwanglin New Material Technology Co., Ltd., the company's registered capital of one hundred million yuan, main technological relying on Shandong Wanglin New Material Technology Technology Ltd. and its subordinate production bases.