Product Properties: WL-5003 is a universal unsaturated polyester resin with median viscosity, high-response activity, high mechanical strength, and good surface brightness.
Main Application: WL-5003 resin is widely used in various glass fiber enhancements. It is mainly used for molding and other molding processes. Suitable for squeezing tent poles, rods, pipelines and other products.
Product specification
performance | scope | unit | standard test |
Exterior | Light -colored transparency | - | GB/T8237-2005 |
Viscosity 25 ℃ | 600-650 | mpa.s | GB/T7193-2008 |
Acid value | 10-18 | mgkoh/g | GB/T2895-2008 |
Solid content | 63-68 | ％ | GB/T7193-2008 |
Gel time 25 ℃ | 4-6 | minutes | GB/T7193-2008 |
Note: 25 ° C Gel Time: 100g resin plus 0.7g Wanglin Promotional and 1.3G Wanglin curing agent (Akzo-Nobel).
Liquid resin performance (typical value)
performance | Value | unit | standard test |
Storage period (not caused, dark parts), 20 ℃ | 3 | month | - |
Resin pouring performance (typical value)
performance | Value | unit | standard test |
Tensile Strength | 70 | MPA | GB/T2567-2008 |
Stretching elastic modulus | 3500 | MPA | GB/T2567-2008 |
Fracture extension | 3.5 | % | GB/T2567-2008 |
Bending strength | 100 | MPA | GB/T2567-2008 |
Bending elastic modulus | 3100 | MPA | GB/T2567-2008 |
Impact strength | 10 | Kj/m2 | GB/T2567-2008 |
Heat distortion temperature | 72 | ℃ | GB/T1634-2004 |
CIThization conditions: room temperature to curing 24 hours, 40 ° C, 60 ° C, 80 ° C for 2 hours each
Test conditions: temperature 23 ± 2 ℃, relative humidity 50 ± 6 %
Instructions and precautions
1. WL-5003 resin should choose the solid system according to factors such as the specific equipment, products, process temperature, and extrusion speed according to its specific equipment, products, process temperature, and extrusion speed. Generally recommended: BPO 0.5%~ 2.0%; TBPB 0.5 ~ 1.5%.
2. The volume contraction rate of unsaturated polyester resin is very large. When pulling the diameter rod material, it is recommended to carry out felt. When pulling the profile, it is recommended to use the low contraction additives provided by Wanglin New Materials such as 3814, 3892, etc., such as 3814, 3892, etc., and so on. Some low-contraction additives are not compatible with 503-1, and there will be layers in use, but this is normal, and it must be added when used.
3.. When using, you must pay attention to controlling the water content of glass fiber, filler, pigment paste and other materials, and pay attention to the compatibility of pigment paste and unsaturated polyester resin.
Storage conditions
1. The resin should be stored in a dry room below 25 ° C before using the resin before using the original packaging (avoid damage to the barrel and barrel).
2. The increase in temperature and light irradiation will significantly reduce the storage period. Direct sunlight and stay away from the thermal source should be avoided during storage.
3.. The unsaturated polyester resin liquid containing the styrene is flammable, and it should be far away from the bright fire when storing. Pay attention to the security data table.
All kinds of data are derived from our in -depth research and extensive practice, so it is completely credible. However, due to the multiple factors of product production, we are not responsible for the actual performance, effects and impacts caused by the above data and the specific application and processing of the products and the processing of the product, and the direct and indirect losses caused by it. Before selecting the above products, please check the product quality, performance indicators, security and other data and confirm it by themselves. At the same time, users should also pay attention to avoid violations of various relevant bills, registered trademarks and patent rights. We are not responsible for this.