8101 is a universal o-benzene resin. Applicable to non-enhanced classes, artificial agate and artificial marble, have excellent coloring performance.
main application
8101 Resin is used in artificial agate and artificial marble, with higher breaking elongation and better process, suitable for rapid demolding, and the articles are not easy to crack.
Product specifications
performance | Scope | unit | standard test |
Exterior | Light and transparent | - | GB / T8237-2005 |
Viscosity 25 ° C | 350-500 | MPA.s | GB / T7193-2008 |
Acid value | 18-24 | Mgkoh / g | GB / T2895-2008 |
Solid content | 66-72 | ％ | GB / T7193-2008 |
Gel time 25 ° C | 4-6 | minutes | GB / T7193-2008 |
Note: 25 ° C gel time: 100 g of a 0.7 Gwen forest promoter and 1.3G Wenlin curing agent.
Liquid resin performance (typical)
performance | Numerical value | unit | standard test |
Storage period (not triggered, dark), 20 ° C | 3 | 月 | - |
Resin casting body (typ)
performance | Numerical value | unit | standard test |
Tensile Strength | 50 | MPA | GB / T2567-2008 |
Tension elastic modulus | 2900 | MPA | GB / T2567-2008 |
Fracture elongation | 5.0 | % | GB / T2567-2008 |
Bending strength | 80 | MPA | GB / T2567-2008 |
Bending elastic modulus | 3200 | MPA | GB / T2567-2008 |
Impact strength | 12 | KJ / M2 | GB / T2567-2008 |
Heat distortion temperature | 50 | ℃ | GB / T1634-2004 |
Curing conditions: 24 hours, 40 ° C, 60 ° C, 80 ° C, respective
2 hours
Test conditions: temperature 23 ± 2 ° C, relative humidity 50 ± 6%
Instructions and precautions
1. The 8101 resin does not contain accelerator, and the appropriate amount of accelerator and curing agent must be added according to the operating environment and operational demand.
2. In order to cure the article from the natural molded surface of the article to air, it is not viscous, and the paraffin-styrene solution is added properly.
3. In order to make the product performance, it can be cured after 80 ° C for a few hours.
Storage conditions
1. The resin should be stored in a dry chamber below 25 ° C before use.
2. The increase in temperature and the light irradiation will significantly reduce the storage period, and the direct sunlight and away from the heat source should be avoided.
3. The unsaturated polyester resin liquid containing styrene is flammable, and it is far from the fire. Note See Secure Data Sheet.
All various data are derived from our in-depth research and extensive practice, and thus is completely credible. However, since the production of products is affected by multiple factors, the actual performance, effects and effects of the above data and product specific application and processing, and the direct and indirect losses produced, we are not responsible. Before selecting the above products, please check the quality, performance indicators, security, and other data of the product, and confirm it. At the same time, users should also pay attention to avoid violations of various relevant bills, registered trademarks and patent rights. We are not responsible for this.
Version number: 2021 / 1.0
Publishing date: 2021/01
Hubei Wanglin New Material Technology Co., Ltd.
Address: South of Xinghua Third Road, Jingmen Chemical Circulating Industry, Hubei Province
Tel: 0533-6236816
Fax: 0533-6236816
product properties
8101 is a universal o-benzene resin. Applicable to non-enhanced classes, artificial agate and artificial marble, have excellent coloring performance.
main application
8101 Resin is used in artificial agate and artificial marble, with higher breaking elongation and better process, suitable for rapid demolding, and the articles are not easy to crack.
Product specifications
performance | Scope | unit | standard test |
Exterior | Light and transparent | - | GB / T8237-2005 |
Viscosity 25 ° C | 350-500 | MPA.s | GB / T7193-2008 |
Acid value | 18-24 | Mgkoh / g | GB / T2895-2008 |
Solid content | 66-72 | ％ | GB / T7193-2008 |
Gel time 25 ° C | 4-6 | minutes | GB / T7193-2008 |
Note: 25 ° C gel time: 100 g of a 0.7 Gwen forest promoter and 1.3G Wenlin curing agent.
Liquid resin performance (typical)
performance | Numerical value | unit | standard test |
Storage period (not triggered, dark), 20 ° C | 3 | 月 | - |
Resin casting body (typ)
performance | Numerical value | unit | standard test |
Tensile Strength | 50 | MPA | GB / T2567-2008 |
Tension elastic modulus | 2900 | MPA | GB / T2567-2008 |
Fracture elongation | 5.0 | % | GB / T2567-2008 |
Bending strength | 80 | MPA | GB / T2567-2008 |
Bending elastic modulus | 3200 | MPA | GB / T2567-2008 |
Impact strength | 12 | KJ / M2 | GB / T2567-2008 |
Heat distortion temperature | 50 | ℃ | GB / T1634-2004 |
Curing conditions: 24 hours, 40 ° C, 60 ° C, 80 ° C, respective
2 hours
Test conditions: temperature 23 ± 2 ° C, relative humidity 50 ± 6%
Instructions and precautions
1. The 8101 resin does not contain accelerator, and the appropriate amount of accelerator and curing agent must be added according to the operating environment and operational demand.
2. In order to cure the article from the natural molded surface of the article to air, it is not viscous, and the paraffin-styrene solution is added properly.
3. In order to make the product performance, it can be cured after 80 ° C for a few hours.
Storage conditions
1. The resin should be stored in a dry chamber below 25 ° C before use.
2. The increase in temperature and the light irradiation will significantly reduce the storage period, and the direct sunlight and away from the heat source should be avoided.
3. The unsaturated polyester resin liquid containing styrene is flammable, and it is far from the fire. Note See Secure Data Sheet.
All various data are derived from our in-depth research and extensive practice, and thus is completely credible. However, since the production of products is affected by multiple factors, the actual performance, effects and effects of the above data and product specific application and processing, and the direct and indirect losses produced, we are not responsible. Before selecting the above products, please check the quality, performance indicators, security, and other data of the product, and confirm it. At the same time, users should also pay attention to avoid violations of various relevant bills, registered trademarks and patent rights. We are not responsible for this.
Version number: 2021 / 1.0
Publishing date: 2021/01
Hubei Wanglin New Material Technology Co., Ltd.
Address: South of Xinghua Third Road, Jingmen Chemical Circulating Industry, Hubei Province
Tel: 0533-6236816
Fax: 0533-6236816