WL-9007
旺林
product properties
WL-9007 is a phenolic ethylene resin with high temperature resistance and excellent mechanical properties. The thermal deformation temperature of the FRP can reach more than 210 ° C.
main application
WL-9007 is suitable for making various corrosion-resistant overall glass reinforcement products with high temperature resistance requirements, such as pipelines, containers, storage tanks and other chemical equipment. Suitable for glass reinforced fiber reinforcement processes such as squeezing, winding, spraying, hand paste. Can make metal or concrete surface lining.
Product specification
performance | scope | unit | standard test |
Exterior | Light yellow | - | GB/T8237 |
Viscosity 25 ℃ | 230-370 | mpa.s | GB/T7193 |
Acid value | 6-15 | mgkoh/g | GB/T2895 |
Solid content | 61-66 | % | GB/T7193 |
25 ℃ Gel Time | 8-15 | minutes | GB/T7193 |
Note: 25 ℃ Gel Time: Add 2.5g 4%cobalt and 2.0g m50 to 100g resin.
Line resin performance (typical value)
performance | Value | unit | standard test |
Storage period (not caused, dark parts), 20 ℃ | 3 | 月 | - |
Resin pouring performance (typical value)
performance | Value | unit | standard test |
Tensile Strength | 70 | MPA | GB/T2567 |
Stretching elastic modulus | 3200 | MPA | GB/T2567 |
Fracture extension | 3.5 | % | GB/T2567 |
Bending strength | 125 | MPA | GB/T2567 |
Bending elastic modulus | 3400 | MPA | GB/T2567 |
Impact strength | 14 | Kj/m2 | GB/T2567 |
Heat distortion temperature | 140 | ℃ | GB/T1634 |
CIThization conditions: room temperature to curing for 24 hours, 2 hours after 40 ° C, 60 ° C, and 80 ° C, 0 ° C after 100 ° C for 1h
Test conditions: temperature 23 ± 2 ℃, Relative humidity 50 ± 6 %
Instructions and precautions
1. Factors that affect gel time when actual use include: environmental temperature, humidity, concentration of dynamic agents and promoters, fillers and additives. Suitable for dosage.
2. When construction, please add an appropriate amount of promoter to stir in the resin according to the formula determined by the small test, and then add an appropriate amount of cause and stir. It is strictly forbidden to direct contact with the leading agent and the promotional agent and add simultaneously.
Storage conditions
1. The resin should be stored in a dry room below 25 ° C before using the resin before using the original packaging (avoiding damage to the barrel and barrel).
2. The increase in temperature and light irradiation will significantly reduce the storage period. Direct sunlight and stay away from the thermal source should be avoided during storage.
3.. The unsaturated polyester resin liquid containing the styrene is flammable, and it should be far away from open flames when storing. Pay attention to the security data table.
All kinds of data are derived from our in -depth research and extensive practice, so it is completely credible. However, due to the multiple factors of product production, we are not responsible for the actual performance, effects and impacts caused by the above data and the specific application and processing of the products and the processing of the product, and the direct and indirect losses caused by it. Before selecting the above products, please check the product quality, performance indicators, security and other data and confirm it by themselves. At the same time, users should also pay attention to avoid infringing various relevant bills, registered trademarks and patent rights. We are not responsible for this.
Version number: 2021/1.0
Publishing date: 2021/01
Hubei Wanglin New Material Technology Co., Ltd.
Address: No. 19 Xinghua 3rd Road, Jingmen Chemical Circle Industry, Hubei Province
Tel: 0533-6236816
Fax: 0533-6236816
product properties
WL-9007 is a phenolic ethylene resin with high temperature resistance and excellent mechanical properties. The thermal deformation temperature of the FRP can reach more than 210 ° C.
main application
WL-9007 is suitable for making various corrosion-resistant overall glass reinforcement products with high temperature resistance requirements, such as pipelines, containers, storage tanks and other chemical equipment. Suitable for glass reinforced fiber reinforcement processes such as squeezing, winding, spraying, hand paste. Can make metal or concrete surface lining.
Product specification
performance | scope | unit | standard test |
Exterior | Light yellow | - | GB/T8237 |
Viscosity 25 ℃ | 230-370 | mpa.s | GB/T7193 |
Acid value | 6-15 | mgkoh/g | GB/T2895 |
Solid content | 61-66 | % | GB/T7193 |
25 ℃ Gel Time | 8-15 | minutes | GB/T7193 |
Note: 25 ℃ Gel Time: Add 2.5g 4%cobalt and 2.0g m50 to 100g resin.
Line resin performance (typical value)
performance | Value | unit | standard test |
Storage period (not caused, dark parts), 20 ℃ | 3 | 月 | - |
Resin pouring performance (typical value)
performance | Value | unit | standard test |
Tensile Strength | 70 | MPA | GB/T2567 |
Stretching elastic modulus | 3200 | MPA | GB/T2567 |
Fracture extension | 3.5 | % | GB/T2567 |
Bending strength | 125 | MPA | GB/T2567 |
Bending elastic modulus | 3400 | MPA | GB/T2567 |
Impact strength | 14 | Kj/m2 | GB/T2567 |
Heat distortion temperature | 140 | ℃ | GB/T1634 |
CIThization conditions: room temperature to curing for 24 hours, 2 hours after 40 ° C, 60 ° C, and 80 ° C, 0 ° C after 100 ° C for 1h
Test conditions: temperature 23 ± 2 ℃, Relative humidity 50 ± 6 %
Instructions and precautions
1. Factors that affect gel time when actual use include: environmental temperature, humidity, concentration of dynamic agents and promoters, fillers and additives. Suitable for dosage.
2. When construction, please add an appropriate amount of promoter to stir in the resin according to the formula determined by the small test, and then add an appropriate amount of cause and stir. It is strictly forbidden to direct contact with the leading agent and the promotional agent and add simultaneously.
Storage conditions
1. The resin should be stored in a dry room below 25 ° C before using the resin before using the original packaging (avoiding damage to the barrel and barrel).
2. The increase in temperature and light irradiation will significantly reduce the storage period. Direct sunlight and stay away from the thermal source should be avoided during storage.
3.. The unsaturated polyester resin liquid containing the styrene is flammable, and it should be far away from open flames when storing. Pay attention to the security data table.
All kinds of data are derived from our in -depth research and extensive practice, so it is completely credible. However, due to the multiple factors of product production, we are not responsible for the actual performance, effects and impacts caused by the above data and the specific application and processing of the products and the processing of the product, and the direct and indirect losses caused by it. Before selecting the above products, please check the product quality, performance indicators, security and other data and confirm it by themselves. At the same time, users should also pay attention to avoid infringing various relevant bills, registered trademarks and patent rights. We are not responsible for this.
Version number: 2021/1.0
Publishing date: 2021/01