WL-9001
WangLin NM
product properties
WL-9001 It is a bisphenol -type ethylene ethylene resin. At the same time, the resin has the advantages of high strength, good thermal resistance, and wide applicability.
main application
WL-9001 resin is mainly used in anti-corrosion equipment in papermaking, medicine, power generation, pipelines, steel and other fields.
Product specification
performance | scope | unit | standard test |
Exterior | Light yellow transparent | - | GB/T8237-2005 |
Viscosity 25 ℃ | 300-500 | mpa.s | GB/T7193-2008 |
Acid value | 6-14 | mgkoh/g | GB/T2895-2008 |
Solid content | 54-60 | ％ | GB/T7193-2008 |
25 ℃ Gel Time | 8-14 | minutes | GB/T7193-2008 |
Note: 25 ° C Gel Time: Add 1.0g of ethylene Program and 1.5G M50 (Akzo-Nobel) to 100g resin.
Line resin performance (typical value)
performance | Value | unit | standard test |
Storage period (not caused, dark parts), 20 ℃ | 3 | 月 | - |
Resin pouring performance (typical value)
performance | Value | unit | standard test |
Tensile Strength | 75 | MPA | GB/T2567-2008 |
Stretching elastic modulus | 3500 | MPA | GB/T2567-2008 |
Fracture extension | 3.5 | % | GB/T2567-2008 |
Bending strength | 130 | MPA | GB/T2567-2008 |
Bending elastic modulus | 3200 | MPA | GB/T2567-2008 |
Impact strength | 14 | Kj/m2 | GB/T2567-2008 |
Heat distortion temperature | 110 | ℃ | GB/T1634-2004 |
CIThization conditions: room temperature to curing for 24 hours, 40 ° C, 60 ° C, 80 ° C after solidification
2 hours, solidify 1h after 100 ° C
Test conditions: temperature 23 ± 2 ℃, relative humidity 50 ± 6 %
Instructions and precautions
1. The product with room temperature solidification must also be cured to achieve better materialized performance. Prior to this, the product needs to pass 24 Clean room temperature. Relaxing conditions are: 80-100 ℃ × 3 ～ 6 Hours (thick products are long). For components for chemical corrosion, post -curing is particularly important.
2. In the process of curing, it is recommended to add 0.2% on the surface of the product Wax of 54-57 ° C of the melting point, match it when joining 10%styrene solution.
3.. It is recommended to use MEKP with low hydrogen peroxide content, or peroxide hebone, or CUHP+ Cobalt liquid solidification system. The surface of the final product with good solidification will not be sticky.
Storage conditions
1. The resin should be stored indoors below 25 ° C before using the resin before using the original packaging (avoid damage to the barrel and barrel).
2. The increase in temperature and light irradiation will significantly reduce the storage period. Direct sunlight and stay away from the thermal source should be avoided during storage.
3.. The unsaturated polyester resin liquid containing the styrene is flammable, and it should be far away from open flames when storing. Pay attention to the security data table.
All kinds of data are derived from our in -depth research and extensive practice, so it is completely credible. However, due to the multiple factors of product production, we are not responsible for the actual performance, effects and impacts caused by the above data and the specific application and processing of the products and the processing of the product, and the direct and indirect losses caused by it. Before selecting the above products, please check the product quality, performance indicators, security and other data and confirm it by themselves. At the same time, users should also pay attention to avoid infringing various relevant bills, registered trademarks and patent rights. We are not responsible for this.
Version number: 2021/1.0
Publishing date: 2021/01
Hubei Wanglin New Material Technology Co., Ltd.
Address: south of Xinghua 3rd Road, Jingmen Chemical Circle Industrial Garden, Hubei Province
Tel: 0533-6236816
Fax: 0533-6236816
product properties
WL-9001 It is a bisphenol -type ethylene ethylene resin. At the same time, the resin has the advantages of high strength, good thermal resistance, and wide applicability.
main application
WL-9001 resin is mainly used in anti-corrosion equipment in papermaking, medicine, power generation, pipelines, steel and other fields.
Product specification
performance | scope | unit | standard test |
Exterior | Light yellow transparent | - | GB/T8237-2005 |
Viscosity 25 ℃ | 300-500 | mpa.s | GB/T7193-2008 |
Acid value | 6-14 | mgkoh/g | GB/T2895-2008 |
Solid content | 54-60 | ％ | GB/T7193-2008 |
25 ℃ Gel Time | 8-14 | minutes | GB/T7193-2008 |
Note: 25 ° C Gel Time: Add 1.0g of ethylene Program and 1.5G M50 (Akzo-Nobel) to 100g resin.
Line resin performance (typical value)
performance | Value | unit | standard test |
Storage period (not caused, dark parts), 20 ℃ | 3 | 月 | - |
Resin pouring performance (typical value)
performance | Value | unit | standard test |
Tensile Strength | 75 | MPA | GB/T2567-2008 |
Stretching elastic modulus | 3500 | MPA | GB/T2567-2008 |
Fracture extension | 3.5 | % | GB/T2567-2008 |
Bending strength | 130 | MPA | GB/T2567-2008 |
Bending elastic modulus | 3200 | MPA | GB/T2567-2008 |
Impact strength | 14 | Kj/m2 | GB/T2567-2008 |
Heat distortion temperature | 110 | ℃ | GB/T1634-2004 |
CIThization conditions: room temperature to curing for 24 hours, 40 ° C, 60 ° C, 80 ° C after solidification
2 hours, solidify 1h after 100 ° C
Test conditions: temperature 23 ± 2 ℃, relative humidity 50 ± 6 %
Instructions and precautions
1. The product with room temperature solidification must also be cured to achieve better materialized performance. Prior to this, the product needs to pass 24 Clean room temperature. Relaxing conditions are: 80-100 ℃ × 3 ～ 6 Hours (thick products are long). For components for chemical corrosion, post -curing is particularly important.
2. In the process of curing, it is recommended to add 0.2% on the surface of the product Wax of 54-57 ° C of the melting point, match it when joining 10%styrene solution.
3.. It is recommended to use MEKP with low hydrogen peroxide content, or peroxide hebone, or CUHP+ Cobalt liquid solidification system. The surface of the final product with good solidification will not be sticky.
Storage conditions
1. The resin should be stored indoors below 25 ° C before using the resin before using the original packaging (avoid damage to the barrel and barrel).
2. The increase in temperature and light irradiation will significantly reduce the storage period. Direct sunlight and stay away from the thermal source should be avoided during storage.
3.. The unsaturated polyester resin liquid containing the styrene is flammable, and it should be far away from open flames when storing. Pay attention to the security data table.
All kinds of data are derived from our in -depth research and extensive practice, so it is completely credible. However, due to the multiple factors of product production, we are not responsible for the actual performance, effects and impacts caused by the above data and the specific application and processing of the products and the processing of the product, and the direct and indirect losses caused by it. Before selecting the above products, please check the product quality, performance indicators, security and other data and confirm it by themselves. At the same time, users should also pay attention to avoid infringing various relevant bills, registered trademarks and patent rights. We are not responsible for this.
Version number: 2021/1.0
Publishing date: 2021/01
Hubei Wanglin New Material Technology Co., Ltd.
Address: south of Xinghua 3rd Road, Jingmen Chemical Circle Industrial Garden, Hubei Province
Tel: 0533-6236816
Fax: 0533-6236816