WL-8810
WangLin NM
product properties
WL-8810 is a phthynalized unsaturated polyester resin. The resin has high viscosity and medium reaction activity. It has good infiltration with the filler, good toughness, and excellent mechanical strength.
main application
WL-8810 resin is used in room temperature and medium-temperature curing artificial quartz slate.
Product specification
performance | scope | unit | standard test |
Exterior | Light -colored transparency | - | GB/T8237-2005 |
Viscosity 25 ℃ | 700-100 | mpa.s | GB/T7193-2008 |
Acid value | 20-27 | mgkoh/g | GB/T2895-2008 |
Solid content | 67-73 | ％ | GB/T7193-2008 |
Gel time 25 ℃ | 6-9 | minutes | GB/T7193-2008 |
Note: 25 ° C Gel Time: 100g resin plus 0.7g Wanglin promoter and 1.3g Wanglin curing agent.
Liquid resin performance (typical value)
performance | Value | unit | standard test |
Storage period (not caused, dark parts), 20 ℃ | 3 | 月 | - |
Resin pouring performance (typical value)
performance | Value | unit | standard test |
Tensile Strength | 50 | MPA | GB/T2567-2008 |
Stretching elastic modulus | 2600 | MPA | GB/T2567-2008 |
Fracture extension | 9.0 | % | GB/T2567-2008 |
Bending strength | 60 | MPA | GB/T2567-2008 |
Bending elastic modulus | 2600 | MPA | GB/T2567-2008 |
Impact strength | 15 | Kj/m2 | GB/T2567-2008 |
Heat distortion temperature | 45 | ℃ | GB/T1634-2004 |
CIThization conditions: room temperature to curing 24 hours, 40 ° C, 60 ° C, 80 ° C for 2 hours each
Test conditions: temperature 23 ± 2 ℃, relative humidity 50 ± 6 %
Instructions and precautions
1. WL-8810 resin does not contain a promotional agent. When used, add an appropriate amount of promotional agent and curing agent according to the operating environment and operating needs.
2. In order to make the natural molding surface of the product and the air does not stick to it, the paraffin-styrene solution is appropriately added.
3.. In order to make the product better, it can be solidified for several hours after 80 ° C.
Storage conditions
1. The resin should be stored in a dry room below 25 ° C before using the resin before using the original packaging (avoid damage to the barrel and barrel).
2. The increase in temperature and light irradiation will significantly reduce the storage period. Direct sunlight and stay away from the thermal source should be avoided during storage.
3.. The unsaturated polyester resin liquid containing the styrene is flammable, and it should be far away from the bright fire when storing. Pay attention to the security data table.
All kinds of data are derived from our in -depth research and extensive practice, so it is completely credible. However, due to the multiple factors of product production, we are not responsible for the actual performance, effects and impacts caused by the above data and the specific application and processing of the products and the processing of the product, and the direct and indirect losses caused by it. Before selecting the above products, please check the product quality, performance indicators, security and other data and confirm it by themselves. At the same time, users should also pay attention to avoid violations of various relevant bills, registered trademarks and patent rights. We are not responsible for this.
Version number: 2021/1.0
Publishing date: 2021/01
Hubei Wanglin New Material Technology Co., Ltd.
Address: south of Xinghua 3rd Road, Jingmen Chemical Circle Industry, Hubei Province
Tel: 0533-6236816
Fax: 0533-6236816
product properties
WL-8810 is a phthynalized unsaturated polyester resin. The resin has high viscosity and medium reaction activity. It has good infiltration with the filler, good toughness, and excellent mechanical strength.
main application
WL-8810 resin is used in room temperature and medium-temperature curing artificial quartz slate.
Product specification
performance | scope | unit | standard test |
Exterior | Light -colored transparency | - | GB/T8237-2005 |
Viscosity 25 ℃ | 700-100 | mpa.s | GB/T7193-2008 |
Acid value | 20-27 | mgkoh/g | GB/T2895-2008 |
Solid content | 67-73 | ％ | GB/T7193-2008 |
Gel time 25 ℃ | 6-9 | minutes | GB/T7193-2008 |
Note: 25 ° C Gel Time: 100g resin plus 0.7g Wanglin promoter and 1.3g Wanglin curing agent.
Liquid resin performance (typical value)
performance | Value | unit | standard test |
Storage period (not caused, dark parts), 20 ℃ | 3 | 月 | - |
Resin pouring performance (typical value)
performance | Value | unit | standard test |
Tensile Strength | 50 | MPA | GB/T2567-2008 |
Stretching elastic modulus | 2600 | MPA | GB/T2567-2008 |
Fracture extension | 9.0 | % | GB/T2567-2008 |
Bending strength | 60 | MPA | GB/T2567-2008 |
Bending elastic modulus | 2600 | MPA | GB/T2567-2008 |
Impact strength | 15 | Kj/m2 | GB/T2567-2008 |
Heat distortion temperature | 45 | ℃ | GB/T1634-2004 |
CIThization conditions: room temperature to curing 24 hours, 40 ° C, 60 ° C, 80 ° C for 2 hours each
Test conditions: temperature 23 ± 2 ℃, relative humidity 50 ± 6 %
Instructions and precautions
1. WL-8810 resin does not contain a promotional agent. When used, add an appropriate amount of promotional agent and curing agent according to the operating environment and operating needs.
2. In order to make the natural molding surface of the product and the air does not stick to it, the paraffin-styrene solution is appropriately added.
3.. In order to make the product better, it can be solidified for several hours after 80 ° C.
Storage conditions
1. The resin should be stored in a dry room below 25 ° C before using the resin before using the original packaging (avoid damage to the barrel and barrel).
2. The increase in temperature and light irradiation will significantly reduce the storage period. Direct sunlight and stay away from the thermal source should be avoided during storage.
3.. The unsaturated polyester resin liquid containing the styrene is flammable, and it should be far away from the bright fire when storing. Pay attention to the security data table.
All kinds of data are derived from our in -depth research and extensive practice, so it is completely credible. However, due to the multiple factors of product production, we are not responsible for the actual performance, effects and impacts caused by the above data and the specific application and processing of the products and the processing of the product, and the direct and indirect losses caused by it. Before selecting the above products, please check the product quality, performance indicators, security and other data and confirm it by themselves. At the same time, users should also pay attention to avoid violations of various relevant bills, registered trademarks and patent rights. We are not responsible for this.
Version number: 2021/1.0
Publishing date: 2021/01
Hubei Wanglin New Material Technology Co., Ltd.
Address: south of Xinghua 3rd Road, Jingmen Chemical Circle Industry, Hubei Province
Tel: 0533-6236816
Fax: 0533-6236816