WL-7002

Availability:
Quantity:

product properties

7002 is a general-purpose o-benzene unsaturated polyester resin having good toughness, wide applicability, and good fiber infiltration.

 

main application

7002 resin is suitable for handling, winding and other production processes, mainly used in winding pipes, hand enhanced layers.

 

 

Product specifications

performance

Scope

unit

standard test

Exterior

Light and transparent

-

GB / T8237-2005

Viscosity 25 ° C

350-500

MPA.s

GB / T7193-2008

Acid value

18-24

Mgkoh / g

GB / T2895-2008

Solid content

64-70

GB / T7193-2008

Gel time 25 ° C

6-8

minutes

GB / T7193-2008

Note: 25 ° C Gel Time: 2.0 g of 1% cobalt and 2.0 g M50 (AKZO-Nobel) were added to 100 g of resin.

 

Liquid resin performance (typical)

performance

Numerical value

unit

standard test

Storage period (not triggered, dark), 20 ° C

3

-

 

 

Resin casting body (typ)

performance

Numerical value

unit

standard test

Tensile Strength

60

MPA

GB / T2567-2008

Tension elastic modulus

2800

MPA

GB / T2567-2008

Fracture elongation

4.2

%

GB / T2567-2008

Bending strength

90

MPA

GB / T2567-2008

Bending elastic modulus

2600

MPA

GB / T2567-2008

Impact strength

8.5

KJ / M2

GB / T2567-2008

Heat distortion temperature

60

GB / T1634-2004

Curing conditions: 24 hours, 40 ° C, 60 ° C, 80 ° C, respective

 2 hours

Test conditions: temperature 23 ± 2 ° C, relative humidity 50 ± 6%

 

Use instructions and precautions

1. 7002 Resin does not include accelerator, and the appropriate amount of accelerator and curing agent must be added according to the operating environment and operational demand.

2. Be sure to control the water content of the material such as glass fiber, filler, pigment paste, etc., pay attention to the compatibility of the pigment paste and the unsaturated polyester resin.

 

Storage conditions

1. The resin should be stored in a dry chamber below 25 ° C before use.

2. The increase in temperature and the light irradiation will significantly reduce the storage period, and the direct sunlight and away from the heat source should be avoided.

3. The unsaturated polyester resin liquid containing styrene is flammable, and it is far from the fire. Note See Secure Data Sheet.

 

 

 All various data are derived from our in-depth research and extensive practice, and thus is completely credible. However, since the production of products is affected by multiple factors, the actual performance, effects and effects of the above data and product specific application and processing, and the direct and indirect losses produced, we are not responsible. Before selecting the above products, please check the quality, performance indicators, security, and other data of the product, and confirm it. At the same time, users should also pay attention to avoid violations of various relevant bills, registered trademarks and patent rights. We are not responsible for this.


 

 Version number: 2021 / 1.0

Publishing date: 2022/02

Hubei Wanglin New Material Technology Co., Ltd.

Address: South of Xinghua Third Road, Jingmen Chemical Circulating Industry, Hubei Province

Tel: 0533-6236816

Fax: 0533-6236816


Previous: 
Next: 
 
Hubei Wanglin New Material Technology Co., Ltd. is a new company specializing in the production of unsaturated polyester resins in Hongwanglin New Material Technology Co., Ltd., the company's registered capital of one hundred million yuan, main technological relying on Shandong Wanglin New Material Technology Technology Ltd. and its subordinate production bases.

Quick Navigation

Product Category

Product Inquiry
All rights reserved2022 Hubei Wanglin New Material Technology Co., Ltd. 鲁ICP2020038246号-1