WL-5005 is a universal unsaturated polyester resin with median viscosity and high-reactive activity, high-pull speed, and high-thermal deformation temperature.
main application
WL-5005 resin is widely used in various glass fiber enhanced molding products.
The main molding process of WL-5005 resin is pulling, entangled, RTM, etc.
WL-5005 resin is suitable for profiles with high requirements for rigidity.
Product specification
performance | scope | unit | standard test |
Exterior | Light yellow and transparent | - | GB/T8237-2005 |
Viscosity 25 ℃ | 650-800 | mpa.s | GB/T7193-2008 |
Acid value | 22-28 | mgkoh/g | GB/T2895-2008 |
Solid content | 62-68 | ％ | GB/T7193-2008 |
Gel time 25 ℃ | 8-12 | minutes | GB/T7193-2008 |
Note: 25 ℃ Gel Time: Add 1.0g 1%cobalt and 1.5G M50 to 100g resin.
Liquid resin performance (typical value)
performance | Value | unit | standard test |
Storage period (not caused, dark parts), 20 ℃ | 3 | 月 | - |
Resin pouring performance (typical value)
performance | Value | unit | standard test |
Tensile Strength | 75 | MPA | GB/T2567-2008 |
Stretching elastic modulus | 3600 | MPA | GB/T2567-2008 |
Fracture extension | 2.5 | % | GB/T2567-2008 |
Bending strength | 120 | MPA | GB/T2567-2008 |
Bending elastic modulus | 3300 | MPA | GB/T2567-2008 |
Impact strength | 15 | Kj/m2 | GB/T2567-2008 |
Heat distortion temperature | 80 | ℃ | GB/T1634-2004 |
CIThization conditions: room temperature to curing for 24 hours, 40 ° C, 60 ° C, 80 ° C after curing
2 hours
Test conditions: temperature 23 ± 2 ℃, relative humidity 50 ± 6 %
Instructions and precautions
1. The WL-5005 resin should choose the solid system according to factors such as the specific equipment, products, process temperature, and extrusion speed of the WL-5005 resin. Generally recommended: BPO 0.5%~ 2.0%; TBPB 0.5 ~ 1.5%.
2. The volume contraction rate of unsaturated polyester resin is very large. When pulling the diameter rod material, it is recommended to carry out felt. When pulling the profile, it is recommended to use the low contraction additives provided by Wanglin New Materials such as 3814, 3892, etc., such as 3814, 3892, etc., and so on. Some low -contraction additives are not good enough with 505, and there will be layers when used, but this is normal. You must use it when used.
3.. When using, you must pay attention to controlling the water content of glass fiber, filler, pigment paste and other materials, and pay attention to the compatibility of pigment paste and unsaturated polyester resin.
Storage conditions
1. The resin should be stored in a dry room below 25 ° C before using the resin before using the original packaging (avoid damage to the barrel and barrel).
2. The increase in temperature and light irradiation will significantly reduce the storage period. Direct sunlight and stay away from the thermal source should be avoided during storage.
3.. The unsaturated polyester resin liquid containing the styrene is flammable, and it should be far away from the bright fire when storing. Pay attention to the security data table.
All kinds of data are derived from our in -depth research and extensive practice, so it is completely credible. However, due to the multiple factors of product production, we are not responsible for the actual performance, effects and impacts caused by the above data and the specific application and processing of the products and the processing of the product, and the direct and indirect losses caused by it. Before selecting the above products, please check the product quality, performance indicators, security and other data and confirm it by themselves. At the same time, users should also pay attention to avoid violations of various relevant bills, registered trademarks and patent rights. We are not responsible for this.
Version number: 2021/1.0
Publishing date: 2022/02
Hubei Wanglin New Material Technology Co., Ltd.
Address: south of Xinghua 3rd Road, Jingmen Chemical Circle Industry, Hubei Province
Tel: 0533-6236816
Fax: 0533-6236816
product properties
WL-5005 is a universal unsaturated polyester resin with median viscosity and high-reactive activity, high-pull speed, and high-thermal deformation temperature.
main application
WL-5005 resin is widely used in various glass fiber enhanced molding products.
The main molding process of WL-5005 resin is pulling, entangled, RTM, etc.
WL-5005 resin is suitable for profiles with high requirements for rigidity.
Product specification
performance | scope | unit | standard test |
Exterior | Light yellow and transparent | - | GB/T8237-2005 |
Viscosity 25 ℃ | 650-800 | mpa.s | GB/T7193-2008 |
Acid value | 22-28 | mgkoh/g | GB/T2895-2008 |
Solid content | 62-68 | ％ | GB/T7193-2008 |
Gel time 25 ℃ | 8-12 | minutes | GB/T7193-2008 |
Note: 25 ℃ Gel Time: Add 1.0g 1%cobalt and 1.5G M50 to 100g resin.
Liquid resin performance (typical value)
performance | Value | unit | standard test |
Storage period (not caused, dark parts), 20 ℃ | 3 | 月 | - |
Resin pouring performance (typical value)
performance | Value | unit | standard test |
Tensile Strength | 75 | MPA | GB/T2567-2008 |
Stretching elastic modulus | 3600 | MPA | GB/T2567-2008 |
Fracture extension | 2.5 | % | GB/T2567-2008 |
Bending strength | 120 | MPA | GB/T2567-2008 |
Bending elastic modulus | 3300 | MPA | GB/T2567-2008 |
Impact strength | 15 | Kj/m2 | GB/T2567-2008 |
Heat distortion temperature | 80 | ℃ | GB/T1634-2004 |
CIThization conditions: room temperature to curing for 24 hours, 40 ° C, 60 ° C, 80 ° C after curing
2 hours
Test conditions: temperature 23 ± 2 ℃, relative humidity 50 ± 6 %
Instructions and precautions
1. The WL-5005 resin should choose the solid system according to factors such as the specific equipment, products, process temperature, and extrusion speed of the WL-5005 resin. Generally recommended: BPO 0.5%~ 2.0%; TBPB 0.5 ~ 1.5%.
2. The volume contraction rate of unsaturated polyester resin is very large. When pulling the diameter rod material, it is recommended to carry out felt. When pulling the profile, it is recommended to use the low contraction additives provided by Wanglin New Materials such as 3814, 3892, etc., such as 3814, 3892, etc., and so on. Some low -contraction additives are not good enough with 505, and there will be layers when used, but this is normal. You must use it when used.
3.. When using, you must pay attention to controlling the water content of glass fiber, filler, pigment paste and other materials, and pay attention to the compatibility of pigment paste and unsaturated polyester resin.
Storage conditions
1. The resin should be stored in a dry room below 25 ° C before using the resin before using the original packaging (avoid damage to the barrel and barrel).
2. The increase in temperature and light irradiation will significantly reduce the storage period. Direct sunlight and stay away from the thermal source should be avoided during storage.
3.. The unsaturated polyester resin liquid containing the styrene is flammable, and it should be far away from the bright fire when storing. Pay attention to the security data table.
All kinds of data are derived from our in -depth research and extensive practice, so it is completely credible. However, due to the multiple factors of product production, we are not responsible for the actual performance, effects and impacts caused by the above data and the specific application and processing of the products and the processing of the product, and the direct and indirect losses caused by it. Before selecting the above products, please check the product quality, performance indicators, security and other data and confirm it by themselves. At the same time, users should also pay attention to avoid violations of various relevant bills, registered trademarks and patent rights. We are not responsible for this.
Version number: 2021/1.0
Publishing date: 2022/02
Hubei Wanglin New Material Technology Co., Ltd.
Address: south of Xinghua 3rd Road, Jingmen Chemical Circle Industry, Hubei Province
Tel: 0533-6236816
Fax: 0533-6236816