  • WL-4002C

Product Description 

WL-4002C is a pre-accelerated general-purpose unsaturated polyester resin. The resin has the  advantages of low viscosity, good glass fiber impregnation, low shrinkage, good toughness and  high strength. 


Application 

WL-4002C resin is vacuum infusion, which is widely used in automotive parts, cooling  towers and other fields.

 

properties

performance

Parameter

unit

standard test

Exterior

light green transparent

-

GB/T8237

Viscosity 25℃

160-200

mPa.s

GB/T7193

Acid value

16-24

mgKOH/g

GB/T2895

solid content

62-68

%

GB/T7193

Gel time 25℃

40-60

minutes

GB/T7193

Note: 25℃ gel time: add 2.0g Wanglin accelerator and 2.0g to 100g resin

Wanglin curing agent.



Liquid Resin Properties (Typical Values)

performance

numerical value

unit

standard test

Storage period (uninitiated, dark place)

3

month

-



Resin cast body properties (typical values)

performance

Parameter

unit

standard test

Tensile Strength

55

MPa

GB/T2567-2008

Tensile elastic modulus

3000

MPa

GB/T2567-2008

Elongation at break

2.5

%

GB/T2567-2008

Bending strength

90

MPa

GB/T2567-2008

bending elastic modulus

3000

MPa

GB/T2567-2008

Impact strength

7

KJ/m2

GB/T2567-2008

Heat distortion temperature

78

GB/T1634-2004

Curing conditions: 24 hours at room temperature, 40°C, 60°C, and 80°C.

 2 hours

Test conditions: temperature 23±2 ℃, relative humidity 50±6%

 


Instructions and precautions for use

1.   WL-4002C resin contains accelerator. When using it, an appropriate amount of accelerator and curing agent must be added according to the operating environment and operating needs.

2.   When using, be sure to control the moisture content of materials such as glass fiber, fillers, and pigment pastes, and pay attention to the compatibility of the pigment paste and unsaturated polyester resin.


Storage conditions

1.   Before use, the resin should be stored in the original packaging (to avoid opening and damaging the barrel) in a dry room below 25°C.

2.   The increase in temperature and exposure to light will significantly shorten the storage period. Avoid direct sunlight and keep away from heat sources during storage.

3.   Unsaturated polyester resin liquid containing styrene is flammable and should be stored away from open flames.Please refer to the safety data sheet.


 

 All various data are derived from our in-depth research and extensive practice and are therefore completely trustworthy.However, since the production of products is affected by multiple factors, we are not responsible for the actual performance, effects and effects caused by the above data and the specific application and processing of the products, as well as the resulting direct and indirect losses.Before selecting the above products, users are requested to check and confirm the relevant product quality, performance indicators, safety and other data themselves.At the same time, users should also pay attention to avoid infringing various relevant laws, registered trademarks and patent rights.We are not responsible for this.



Version No.:2021/1.0 

Publication date:2021/01 

Shandong Wanglin New Material Co., Ltd. 

Add:Chemical Industry Park, Economic Development Zone, Pingyuan County, Dezhou City, Shandong Province T:(86)15863477700 

E: scott.cui@wl-upr.com 



Previous: 
Next: 
 
Hubei Wanglin New Material Technology Co., Ltd. is a new company specializing in the production of unsaturated polyester resins in Hongwanglin New Material Technology Co., Ltd., the company's registered capital of one hundred million yuan, main technological relying on Shandong Wanglin New Material Technology Technology Ltd. and its subordinate production bases.

Quick Navigation

Product Category

Product Inquiry
All rights reserved2022 Hubei Wanglin New Material Technology Co., Ltd. 鄂ICP备2021007343号-1