WL-3110C
Product Description
WL-3110C is a corrosion-resistant unsaturated polyester resin with medium viscosity, high reactivity, high heat resistance, high mechanical strength and high elongation at break.
Application
WL-3110C is suitable for pipes, storage tanks, automotive parts, ships and double-wall oil tanks that require high mechanical properties. It is used in winding, hand lay-up, RTM and other molding processes.
Properties
performance | Parameter | unit | standard test |
Exterior | yellow transparent | - | GB/T8237 |
Viscosity 25℃ | 900-1000 | mPa.s | GB/T7193 |
Acid value | 10-16 | mgKOH/g | GB/T2895 |
solid content | 60-66 | ％ | GB/T7193 |
Gel time 25℃ | 9-14 | minutes | GB/T7193 |
Note: 25℃ gel time: add 1.0g 1% cobalt and 1.5g M50 (AKZO-Nobel) to 100g resin.
Liquid Resin Properties (Typical Values)
performance | numerical value | unit | standard test |
Storage period (uninitiated, dark place), 20℃ | 3 | month | - |
Resin cast body properties (typical values)
performance | Parameter | unit | standard test |
Tensile Strength | 70 | MPa | GB/T2567 |
Tensile modulus of elasticity | 3200 | MPa | GB/T2567 |
Elongation at break | 3.0 | % | GB/T2567 |
Bending strength | 120 | MPa | GB/T2567 |
bending elastic modulus | 3300 | MPa | GB/T2567 |
Impact strength | 12 | KJ/m2 | GB/T2567 |
Heat distortion temperature | 85 | ℃ | GB/T1634 |
Curing conditions: 24 hours at room temperature, 40°C, 60°C, and 80°C.
2 hours, 1 hour post-curing at 100°C
Test conditions: temperature 23±2 ℃, Relative humidity 50±6%
Instructions and attentions
1. WL-3110C resin does not contain accelerators. When using, appropriate amounts of accelerators and curing agents must be added according to the operating environment and operating requirements.
2. When using, be sure to control the water content of fillers, pigment pastes and other materials, and pay attention to the compatibility of pigment pastes with unsaturated polyester resins.
Storage conditions
1. Before use, the resin should be stored in the original packaging (to avoid opening and damaging the barrel) in a dry room below 25°C.
2. The increase in temperature and exposure to light will significantly shorten the storage period. Avoid direct sunlight and keep away from heat sources during storage.
3. Unsaturated polyester resin liquid containing styrene is flammable and should be stored away from open flames.Please refer to the safety data sheet.
All various data are derived from our in-depth research and extensive practice and are therefore completely trustworthy.However, since the production of products is affected by multiple factors, we are not responsible for the actual performance, effects and effects caused by the above data and the specific application and processing of the products, as well as the resulting direct and indirect losses.Before selecting the above products, users are requested to check and confirm the relevant product quality, performance indicators, safety and other data themselves.At the same time, users should also pay attention to avoid infringing various relevant laws, registered trademarks and patent rights.We are not responsible for this.
Version number: 2021/1.0
Publication date: 2021/01
Shandong Wanglin New Material Co., Ltd.
Address: Chemical Park, Economic Development Zone, Pingyuan County, Dezhou City, Shandong Province
T：(86)15863477700
E：scott.cui@wl-upr.com
Product Description
WL-3110C is a corrosion-resistant unsaturated polyester resin with medium viscosity, high reactivity, high heat resistance, high mechanical strength and high elongation at break.
Application
WL-3110C is suitable for pipes, storage tanks, automotive parts, ships and double-wall oil tanks that require high mechanical properties. It is used in winding, hand lay-up, RTM and other molding processes.
Properties
performance | Parameter | unit | standard test |
Exterior | yellow transparent | - | GB/T8237 |
Viscosity 25℃ | 900-1000 | mPa.s | GB/T7193 |
Acid value | 10-16 | mgKOH/g | GB/T2895 |
solid content | 60-66 | ％ | GB/T7193 |
Gel time 25℃ | 9-14 | minutes | GB/T7193 |
Note: 25℃ gel time: add 1.0g 1% cobalt and 1.5g M50 (AKZO-Nobel) to 100g resin.
Liquid Resin Properties (Typical Values)
performance | numerical value | unit | standard test |
Storage period (uninitiated, dark place), 20℃ | 3 | month | - |
Resin cast body properties (typical values)
performance | Parameter | unit | standard test |
Tensile Strength | 70 | MPa | GB/T2567 |
Tensile modulus of elasticity | 3200 | MPa | GB/T2567 |
Elongation at break | 3.0 | % | GB/T2567 |
Bending strength | 120 | MPa | GB/T2567 |
bending elastic modulus | 3300 | MPa | GB/T2567 |
Impact strength | 12 | KJ/m2 | GB/T2567 |
Heat distortion temperature | 85 | ℃ | GB/T1634 |
Curing conditions: 24 hours at room temperature, 40°C, 60°C, and 80°C.
2 hours, 1 hour post-curing at 100°C
Test conditions: temperature 23±2 ℃, Relative humidity 50±6%
Instructions and attentions
1. WL-3110C resin does not contain accelerators. When using, appropriate amounts of accelerators and curing agents must be added according to the operating environment and operating requirements.
2. When using, be sure to control the water content of fillers, pigment pastes and other materials, and pay attention to the compatibility of pigment pastes with unsaturated polyester resins.
Storage conditions
1. Before use, the resin should be stored in the original packaging (to avoid opening and damaging the barrel) in a dry room below 25°C.
2. The increase in temperature and exposure to light will significantly shorten the storage period. Avoid direct sunlight and keep away from heat sources during storage.
3. Unsaturated polyester resin liquid containing styrene is flammable and should be stored away from open flames.Please refer to the safety data sheet.
All various data are derived from our in-depth research and extensive practice and are therefore completely trustworthy.However, since the production of products is affected by multiple factors, we are not responsible for the actual performance, effects and effects caused by the above data and the specific application and processing of the products, as well as the resulting direct and indirect losses.Before selecting the above products, users are requested to check and confirm the relevant product quality, performance indicators, safety and other data themselves.At the same time, users should also pay attention to avoid infringing various relevant laws, registered trademarks and patent rights.We are not responsible for this.
Version number: 2021/1.0
Publication date: 2021/01
Shandong Wanglin New Material Co., Ltd.
Address: Chemical Park, Economic Development Zone, Pingyuan County, Dezhou City, Shandong Province
T：(86)15863477700
E：scott.cui@wl-upr.com