WL-1911C is a general-purpose unsaturated polyester resin with high reactivity and good wettability. It also has the advantages of good toughness and wide applicability.
Application
WL-1911C resin is suitable for hand lay-up, winding, continuous plate making and other production processes, and is mainly used in pipelines, storage tanks, and machine-made plates.
Properties
performance | Parameter | unit | standard test |
Exterior | light color transparent | - | GB/T8237 |
Viscosity 25℃ | 350-450 | mPa.s | GB/T7193 |
Acid value | 24-30 | mgKOH/g | GB/T2895 |
solid content | 62-68 | ％ | GB/T7193 |
Gel time 27℃ | 10-20 | minutes | GB/T7193 |
Note: 27℃ gel time: add 2.0g 1% cobalt and 2.0g M50 (AKZO-Nobel) to 100g resin.
Liquid Resin Properties (Typical Values)
performance | numerical value | unit | standard test |
Storage period (uninitiated, dark place), 20℃ | 3 | month | - |
Resin cast body properties (typical values)
performance | Parameter | unit | standard test |
Tensile Strength | 70 | MPa | GB/T2567 |
Tensile modulus of elasticity | 3200 | MPa | GB/T2567 |
Elongation at break | 4.0 | % | GB/T2567 |
Bending strength | 110 | MPa | GB/T2567 |
bending elastic modulus | 3400 | MPa | GB/T2567 |
Impact strength | 8.5 | KJ/m2 | GB/T2567 |
Heat distortion temperature | 75 | ℃ | GB/T1634 |
Curing conditions: 24 hours at room temperature, 40°C, 60°C, and 80°C.
2 hours
Test conditions: temperature 23±2 ℃, relative humidity 50±6%
Instructions and attentions
1. WL-1911C resin does not contain accelerators. When using, appropriate amounts of accelerators and curing agents must be added according to the operating environment and operating requirements.
2. When using, be sure to control the water content of materials such as glass fiber, filler, pigment paste, etc., and pay attention to the compatibility of pigment paste with unsaturated polyester resin.
Storage conditions
1. Before use, the resin should be stored in the original packaging (to avoid opening and damaging the barrel) in a dry room below 25°C.
2. The increase in temperature and exposure to light will significantly shorten the storage period. Avoid direct sunlight and keep away from heat sources during storage.
3. Unsaturated polyester resin liquid containing styrene is flammable and should be stored away from open flames.Please refer to the safety data sheet.
All various data are derived from our in-depth research and extensive practice and are therefore completely trustworthy.However, since the production of products is affected by multiple factors, we are not responsible for the actual performance, effects and impacts caused by the above data and the specific application and processing of the products, as well as the resulting direct and indirect losses.Before selecting the above products, users are requested to check and confirm the relevant product quality, performance indicators, safety and other data themselves.At the same time, users should also pay attention to avoid infringing various relevant laws, registered trademarks and patent rights.We are not responsible for this.
VersionNo.：2021/1.0
Publicationdate：2021/02
Shandong Wanglin New Material Co., Ltd.
Address:Chemical Park, Economic Development Zone, PingyuanCounty, DezhouCity, Shandong Pr ovince
T：(86)15863477700
E：scott.cui@wl-upr.com
Product Description
WL-1911C is a general-purpose unsaturated polyester resin with high reactivity and good wettability. It also has the advantages of good toughness and wide applicability.
Application
WL-1911C resin is suitable for hand lay-up, winding, continuous plate making and other production processes, and is mainly used in pipelines, storage tanks, and machine-made plates.
Properties
performance | Parameter | unit | standard test |
Exterior | light color transparent | - | GB/T8237 |
Viscosity 25℃ | 350-450 | mPa.s | GB/T7193 |
Acid value | 24-30 | mgKOH/g | GB/T2895 |
solid content | 62-68 | ％ | GB/T7193 |
Gel time 27℃ | 10-20 | minutes | GB/T7193 |
Note: 27℃ gel time: add 2.0g 1% cobalt and 2.0g M50 (AKZO-Nobel) to 100g resin.
Liquid Resin Properties (Typical Values)
performance | numerical value | unit | standard test |
Storage period (uninitiated, dark place), 20℃ | 3 | month | - |
Resin cast body properties (typical values)
performance | Parameter | unit | standard test |
Tensile Strength | 70 | MPa | GB/T2567 |
Tensile modulus of elasticity | 3200 | MPa | GB/T2567 |
Elongation at break | 4.0 | % | GB/T2567 |
Bending strength | 110 | MPa | GB/T2567 |
bending elastic modulus | 3400 | MPa | GB/T2567 |
Impact strength | 8.5 | KJ/m2 | GB/T2567 |
Heat distortion temperature | 75 | ℃ | GB/T1634 |
Curing conditions: 24 hours at room temperature, 40°C, 60°C, and 80°C.
2 hours
Test conditions: temperature 23±2 ℃, relative humidity 50±6%
Instructions and attentions
1. WL-1911C resin does not contain accelerators. When using, appropriate amounts of accelerators and curing agents must be added according to the operating environment and operating requirements.
2. When using, be sure to control the water content of materials such as glass fiber, filler, pigment paste, etc., and pay attention to the compatibility of pigment paste with unsaturated polyester resin.
Storage conditions
1. Before use, the resin should be stored in the original packaging (to avoid opening and damaging the barrel) in a dry room below 25°C.
2. The increase in temperature and exposure to light will significantly shorten the storage period. Avoid direct sunlight and keep away from heat sources during storage.
3. Unsaturated polyester resin liquid containing styrene is flammable and should be stored away from open flames.Please refer to the safety data sheet.
All various data are derived from our in-depth research and extensive practice and are therefore completely trustworthy.However, since the production of products is affected by multiple factors, we are not responsible for the actual performance, effects and impacts caused by the above data and the specific application and processing of the products, as well as the resulting direct and indirect losses.Before selecting the above products, users are requested to check and confirm the relevant product quality, performance indicators, safety and other data themselves.At the same time, users should also pay attention to avoid infringing various relevant laws, registered trademarks and patent rights.We are not responsible for this.
VersionNo.：2021/1.0